A series of noble metal high entropy alloys with up to six constituent elements has been produced by casting. PtPdRhIrCuNi forms single-phase face-centered cubic solid solution, and its stability is confirmed by annealing experiments. This alloy deforms homogeneously to ~30% to a high ultimate compression strength of 1839MPa. We discuss rules for the formation of single-phase solid solution.
-
The glass forming ability (GFA) of metallic glasses (MGs) is quantified by the critical cooling rate (R C). Despite its key role in MG research, experimental challenges have limited measured R C to a minute fraction of known glass formers. We present a combinatorial approach to directly measure R C for large compositional ranges. This is realized through the use of compositionally-graded alloy libraries, which were photo-thermally heated by scanning laser spike annealing of an absorbing layer, then melted and cooled at various rates. Coupled with X-ray diffraction mapping, GFA is determined from direct R C measurements. We exemplify this technique for the Au-Cu-Si system, where we identify Au56Cu27Si17 as the alloy with the highest GFA. In general, this method enables measurements of R C over large compositional areas, which is powerful for materials discovery and, when correlating with chemistry and other properties, for a deeper understanding of MG formation.