Supercapacitors or electrochemical capacitors are receiving greater interest because of their high-power density, long life, and low maintenance. We have synthesized CuS nanoparticles and graphene oxide (CuS-GO) nanocomposites for supercapacitor applications because of their low cost and excellent electrochemical properties. The phase purity of each material was determined using powder XRD studies. The bandgap was determined by UV-visible spectrophotometric studies. Scanning electron microscope and transmission electron microscope images revealed the nano-scale morphology of the synthesized particles. All the electrochemical measurements were conducted in a standard three-electrode configuration, using a platinum wire as the counter electrode and Hg/HgO as the reference electrode. CuS and its composites with graphene oxide on nickel foam were used as working electrodes. All the electrochemical measurements were performed in 3M KOH solution. The CuS-GO nanocomposite electrode showed a specific capacitance of 250 F/g, 225 F/g, 182 F/g, 166 F/g, 161 F/g, and 158 F/g at a current density of 0.5 A/g, 1 A/g, 5 A/g, 10 A/g, 15 A/g, and 20 A/g, respectively. CuS-GO electrodes showed a specific capacitance retention of 70% after 5000 charge-discharge cycles at a current density of 5 A/g. © 2020 Author(s).
-
Graphene oxide (GO)/MnO2 nanocomposites were synthesized by adding KMnO4 in a solution of water and ethanol (3:1), containing 10 mg of GO. Brown precipitates were obtained after a continuous stirring for 1 hr. The precipitates were then washed with deionized water (DI) water and dried to obtain the MnO2-GO nanocomposites. Pure MnO2 was also synthesized using the same method without GO for the comparison. X-ray diffraction pattern confirm δ-MnO2 type of MnO2 with birnessite type MnO2 structure. The TEM images show the average diameter of MnO2 nanorods as 15 nm. Electrochemical characterizations were carried out in an aqueous solution of 3M KOH. Charge-discharge studies were carried out between 1A/g to 20 A/g current range. The MnO2-GO nanocomposites showed improved electrochemical performances. The capacitance of MnO2 and MnO2-GO electrodes was found to be as 300 F/g, and 350 F/g, respectively at a current of 0.5 A/g. © 2019 Materials Research Society.
-
CuS and CuS-rGO nanocomposites were synthesized by the hydrothermal method. The synthesized CuS and rGO-CuS nanocomposite materials were physically characterized by X-ray diffraction (XRD) and scanning electron microscope (SEM) and were evaluated electrochemically for supercapacitor applications. The specific capacitance of CuS was determined to be 207 F/g, 150 F/g, and 97 F/g at a current density of 0.5 A/g, 5 A/g, and 20 A/g, respectively. The rGO-CuS nanocomposite showed improved specific capacitance of 350 F/g, 251 F/g, and 149 F/g at a current density of 0.5 A/g, 5 A/g, and 20 A/g, respectively.
Explore
Resource type
- Journal Article (2)
- Preprint (1)
Publication year
-
Between 2000 and 2026
(3)
-
Between 2010 and 2019
(1)
- 2019 (1)
- Between 2020 and 2026 (2)
-
Between 2010 and 2019
(1)
Resource language
- English (3)