For thin film devices based on coupling ferroelectric polarization to charge carriers in semiconductors, the role of the interface is critical. To elucidate this role, we use synchrotron x-ray diffraction to determine the interface structure of epitaxial SrTiO3 grown on the (001) surface of Si. The average displacement of the O octahedral sublattice relative to the Sr sublattice determines the film polarization and is measured to be about 0.05 nm toward the Si, with Ti off-center displacements 0.009 nm away from the substrate. Measurements of films with different boundary conditions on the top of the SrTiO3 show that the polarization at the SrTiO3 /Si interface is dominated by oxide-Si chemical interactions. © 2010 American Institute of Physics.